Product Description
The light weight mullite bricks contains high porosity, which can save more heat and therefore reduces the cost of fuel. Meanwhile the light weight means less heat storage capacity, so less time is required when the kiln is heated or cooled. Faster periodic operation is workable. It can be applied at the temperature range from 900 to 1600 ℃. It is mainly used as kiln lining in high temperature(less than 1700 ℃) kilns of ceramics, petrochemical, metallurgy and machinery.Typical Features
Low thermal conductivity, low heat capacity, low impurity content High strength, excellent thermal shock resistance, erosion resistance Accurate dimensionTypical Application
Ceramics roller kiln and shuttle kiln: standard brick, roller passage hole brick, hanger brick, Metallurgy industry: hot blast furnace; inner lining of foundry kilns Power industry: power generation and fluidised bed equipment Electrolytic Aluminium industry: kiln inner liningTypical product properties
| Mullite light-weight insulation bricks Product Properties | ||||||
| Product Code | MYJM-23 | MYJM-26 | MYJM-28 | MYJM-30 | MYJM-32 | |
| Classification Temperature (℃) | 1260 | 1400 | 1500 | 1550 | 1600 | |
| Density (g/cm³) | 550 | 800 | 900 | 1000 | 1100 | |
| Permanent linear thrinkage (℃×8h) | 0.3 (1260) | 0.4 (1400) | 0.6 (1500) | 0.6 (1550) | 0.6 (1600) | |
| compressive strength(Mpa) | 1.1 | 1.9 | 2.5 | 2.8 | 3 | |
| Repture strength(Mpa) | 0.8 | 1.2 | 1.4 | 1.6 | 1.8 | |
| Thermal conductivity (W/m.k) (350℃) | 0.15 | 0.26 | 0.33 | 0.38 | 0.43 | |
| Chemical composition (%) | Al2O3 | 40 | 54 | 62 | 74 | 80 |
| Fe2O3 | 1.2 | 0.9 | 0.8 | 0.7 | 0.5 | |
| Note: Test data shown are average results of tests conducted under standard procedures and are subject to variation. Results should not be used for specification purposes. The products listed comply to ASTM C892. | ||||||